Stoneware paper clay bearing grog 0-0.2 mm. Formulated for artistic ceramics, it is unique for modelling, thanks to its exceptional plasticity. It is specially suitable for making impossible shapes with difficult drying. The presence of paper fibres inside avoid formation of cracks and problems...
SIO-2 - Stoneware Paper Clay - PCLI (0-0.2mm) - 1100-1260°C - 12.5Kg
€22.00
Stoneware paper clay bearing grog 0-0.2 mm. Formulated for artistic ceramics, it is unique for modelling, thanks to its exceptional plasticity. It is specially suitable for making impossible shapes with difficult drying. The presence of paper fibres inside avoid formation of cracks and problems...
Stoneware paper clay bearing grog 0-0.2 mm. Formulated for artistic ceramics, it is unique for modelling, thanks to its exceptional plasticity. It is specially suitable for making impossible shapes with difficult drying. The presence of paper fibres inside avoid formation of cracks and problems of deformations, and leads PCL clay to surprising artistic possibilities. Odourless. Available in extruded body (moist form).
- Firing range: 1100-1260ºC.
- Biscuit temperature: 1000ºC.
- Water content: 24%.
- Plasticity (IP Atterberg): 27.
- Carbonate content (CaCO3): 0%.
- Drying shrinkage: 7.2%.
- Firing shrinkage (1200ºC): 6.0%.
- Porosity (water absorption at 1200ºC): 4.2%.
- Dry bending strength: 5.2 N/mm2.
- Fired bending strength (1200ºC): 39.5 N/mm2.
- Thermal coefficient (25-500ºC): 53.7x10^-7ºC^-1.